UL Lead-freeJacketing Compound

环保型UL护套料

NB-60(H) NB-75(H) NB-90(H) NB-105(H)

Product Description产品描述
UL lead-free jacketing compounds are granular compound which are manufactured through mixing, plasticizing and pelletizing processes. They regard advanced PVC resin as the basic raw materials, and add plasticizer, stabilizer and other accessory ingredients.
环保型UL系列护套料产品是以优质聚氯乙烯树脂为基料，加入特种增塑剂、稳定剂等助剂，经混合、塑化、造粒而成的粒状电缆料。

Characteristics and Application 特点及用途
These products have excellent mechanical and physical properties, electrical property and good processability. They can meet environment rules in RoHS Standard. All their properties meet UL1581 Standard. They are mainly used for the jacketing of soft wires and equipment cables.
产品具有良好的机械物理性能和电性能，加工性能优异，符合RoHS环保标准。性能符合UL1581等标准的要求，主要用于软线和装备线的护套。

Processing Indicator加工工艺
Recommend to use of single-screw extruders with L/D= 20-25.
建议使用普通长径比为20-25的单螺杆挤出机进行生产。

Model 牌号	Machine Barrel Temperature 机筒温度	Molding Temperature 机头温度
NB-60(H)/NB-75(H)/ NB-90(H)/NB-105(H)	145-180℃	170-180℃

Physical and Electrical Properties
机械物理性能及电性能指标

Item 试验项目	Unit 单位	Technical Requirements 技术要求
Item 试验项目	Unit 单位	NB-60(H)	NB-75(H)	NB-90(H)	NB-105(H)
Tensile Strength 拉伸强度	MPa	≥12.5	≥12.5	≥12.5	≥12.5
Elongation at Break 断裂伸长率	%	≥180	≥180	≥180	≥180
200℃Thermal Stability 200℃时热稳定时间	min	≥60	≥60	≥80	≥120
Oxygen Index 氧指数	%	≥28	≥28	≥28	≥28
Flame-retardant 难燃性（94V-0）	/	pass	pass	pass	pass
Brittle Temperature with Impact 冲击脆化温度	℃	-20	-20	-25	-20
20℃Volume Resistivity 20℃时体积电阻率	Ω.m	≥1.0×10⁸	≥1.0×10⁸	≥1.0×10⁸	≥1.0×10⁸
Dielectric Strength 介电强度	MV/m	≥20	≥20	≥20	≥20
Thermal Aging 热老化试验	\	100℃×168h	113℃×168h	121℃×168h	136℃×168h
Retention Rate of Tensile Strength 拉伸强度残留率	%	≥75	≥75	≥75	≥75
ResidualRate of Elongation atBreak 断裂伸长率残留率	%	≥65	≥65	≥65	≥65