Description and Application 产品描述和用途
FWYR125 is a kind of soft and oil-resistant irradiation cross-linkable halogen-free elastomeric compound with the highest working temperature at 125℃. It has good mechanical property, electrical property, flame retardant property and processability and especially excellent for oil resistant and soft performances. It is specially suitalbe forthe jacketing and insulation which have strict elastomeric property requirements. It also can be used for other cables which have high temperature requirements.
FWYR125是一种辐照交联柔软耐油无卤弹性体,其具有优良的物理机械性能,电性能,阻燃性能以及加工性能,更为突出的是其具有较好的耐油性和柔软性能,特别适用于对弹性要求较高的绝缘,护套上,也可用于其它有高温要求的电缆上。产品最高使用温度为125℃。
Processing Indicator 加工工艺
Recommend to use special screw for low-smoke halogen-free compound with L/D=20-25.
采用低烟无卤专用螺杆,长径比L/D=20-25。
Model
牌号 |
Machine Barrel Temperature
机筒温度 |
Molding Temprature
机头温度 |
FWYR125 |
130-150℃ |
145-160℃ |
Physical and Electrical Properties 物理及电性能指标
Item
试验项目 |
Unit
单位 |
Specification
技术要求 |
Density
密度 |
g/cm3 |
≤1.45 |
Tensile Strength
拉伸强度 |
MPa |
≥10 |
Elongation at Break
断裂伸长率 |
% |
≥180 |
Aging Conditions
空气热老化条件 |
/ |
158℃×168h |
Reserved Tensile Strength
拉伸强度保留率 |
% |
≥70 |
Reserved Elongation at Break
断裂伸长率保留率 |
% |
≥70 |
Dielectric Strength
介电强度 |
MV/m |
≥20 |
Brittle Temperature With Low Temperature Impact
冲击脆化温度 |
℃ |
-40 |
20℃Volume Resistivity
20℃体积电阻率 |
Ω. m |
≥1.0×1011 |
Oxygen Index
氧指数 |
% |
≥30 |
HCL Gas Evolution
HCL气体发生量 |
Mg/g |
≤5.0 |
PH Value
PH值 |
/ |
≥4.3 |
Smoke Density烟密度
– No-flame Mode无焰模式
– Flame Mode有焰模式 |
Ds max |
≤300
≤150 |
Conductivity
电导率 |
uS/mm |
≤10 |
Toxicity Index
毒性指数 |
/ |
≤5.0 |
Hardness
硬度 |
Shore A |
80-90 |
Hot Set Test Condition
热延伸实验条件
200℃×0.2MPa×15min |
Hot Elongation
负荷下伸长率 |
% |
≤80 |
Set
冷却后永久形变 |
% |
≤5 |
Oil-
Resistant Properties
耐油性能
902# 100℃×70h |
retention of Tensile Strength
拉伸强度保留率 |
% |
≥40 |
Retention for Elongation at Break
断裂伸长率保留率 |
% |
≥40 |
Oil Resistant Properties
耐油性能
903# 70℃×168h |
Retention of Tensile Strength
拉伸强度保留率 |
% |
≥40 |
Retention for Elongation at Break
断裂伸长率保留率 |
% |
≥40 |
Suggested irradiation dose:12-18 mega-tera.建议的辐照剂量为:12-18兆拉
Attentions 注意事项:
1)The compound should be dried before using if the package is broken. Once package is open, recommend to run out within 12 hours.
原料破包需烘干后才能使用,材料一经开封,建议12小时之内用完。
2)Please ensure the screw, barrel, hopper are thoroughly cleaned before operation. Avoid bringing impurities while processing.
加工前确保螺杆、机筒、加料斗彻底清理干净,加工过程中严禁带入杂质。
3)If you need a faster extrusion. Please accelerate screw speed gradually to avoid inadequate plasticizing which may cause rough surface of the cables.
如果要快速挤出时,请慢慢逐渐加快螺杆转速,以免塑化不良,电缆表面毛糙。